Effects of Phosphorus and Carbon Contents on Amorphous Forming Ability in Fe-based Amorphous Alloys Used for Thermal Spray Coatings

Abstract

Cost-effective Fe-based amorphous alloys used for thermal spray coatings were developed by varying contents of P and C, and their microstructure, hardness, and corrosion resistance were analyzed. In order to achieve chemical compositions having high amorphous forming ability, thermodynamically calculated phase diagrams of Fe-Al-P-C-B five-component system were used, from which compositions of super-cooled liquid having the lowest driving force of formation of crystalline phases were obtained. The thermodynamic calculation results showed that only phases of Fe3P and Fe3C were formed in the Fe78Al2P(18.3-x)C (x) B-1.7 alloy system. Considering driving force curves of Fe3P and Fe3C, the carbon contents were selected to be 6.90 and 7.47 at. pct, when the thermodynamic calculation temperatures were 697 K (414 A degrees C) and 715 K (442 A degrees C), respectively. According to the microstructural analysis of suction-cast alloys, the Fe78Al2P10.83C7.47B1.7 alloy showed a fully amorphous microstructure, whereas the Fe78Al2P11.40C6.9B1.7 and Fe78Al2P10.3C8.0B1.7 alloys contained Fe3P and Fe3C phases. This Fe78Al2P10.83C7.47B1.7 alloy showed the better hardness and corrosion resistance than those of conventional thermal spray coating alloys, and its production cost could be lowered using cheaper alloying elements, thereby leading to the practical application to amorphous thermal spray coatings. DOI: 10.1007/s11661-013-1615-0 (C) The Minerals, Metals & Materials Society and ASM International 2013