- Effects of equal channel angular pressing temperature on deformation structures of pure Ti
- Authors
- Kim, I; Kim, J; Shin, DH; Lee, CS; Hwang, SK
- Date Issued
- 2003-02-15
- Publisher
- ELSEVIER SCIENCE SA
- Abstract
- A single equal channel angular pressing at various temperatures (473 to similar to873 K) was conducted on commercially pure titanium in order to investigate the effects of the pressing temperature on the microstructures. Optical and scanning electron microscopy showed that fine shear traces, elongated along the direction of approximately 25degrees inclined to the longitudinal axis of a sample, were well developed over the whole temperature range. Transmission electron microscopy revealed that the shear traces were composed of parallel bands having a width of a submicrometer scale. It was also revealed that the bands of a sample pressed at 473 K resulted from slip but those of samples pressed above 523 K resulted from {10 (1) over bar1} deformation twinning. For the twinned samples, the twin density initially increased with temperature up to 623 K and then decreased at higher temperatures. Contrary to the changes of the twin density, the dislocation density decreased with temperature up to 623 K and then increased. At a pressing temperature of 873 K, fine recrystallized grains were also observed to appear in the vicinity of the shear traces. These anomalous microstructural changes with the pressing temperature were discussed in terms of the characteristics of {10 (1) over bar1} twinning produced by equal channel angular pressing. (C) 2002 Elsevier Science B.V. All rights reserved.
- Keywords
- twin; titanium; transmission electron microscopy; deformation structure; equal channel angular pressing; LOW-CARBON STEEL; CLOSE-PACKED METALS; HCP METALS; TWINNING DISLOCATIONS; PLASTIC-DEFORMATION; GRAIN-REFINEMENT; TITANIUM; CRYSTALLOGRAPHY; MICROSTRUCTURE; SLIP
- URI
- https://oasis.postech.ac.kr/handle/2014.oak/18799
- DOI
- 10.1016/S0921-5093(02)00318-0
- ISSN
- 0921-5093
- Article Type
- Article
- Citation
- MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, vol. 342, no. 1-2, page. 302 - 310, 2003-02-15
- Files in This Item:
- There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.