ALIGNMENT OF LIQUID-CRYSTALS ON RUBBED POLYIMIDE FILMS PREPARED FROM VARIOUS PRECURSOR POLYMERS

Abstract

For poly(p-phenylene biphenyltetracarboximide) (BPDA-PDA) and poly(4,4'-oxydiphenylene pyromellitimide) (PMDA-ODA) in films, surface topographies and molecular in-plane orientations were very sensitive to the precursor origins as well as the softbake and imidization processes. Poby(amic diethyl ester) precursor produced higher surface roughness and lower molecular in-plane orientation in the resultant polyimide than the corresponding poly( amic acid). Rapid softbake and imidization process caused relatively high surface roughness and low molecular in-plane orientation in the resultant film. Rougher surface in the film was more favorably rubbed by rubbing process, causing higher pretilt angle in liquid-crystal molecules in contact with the rubbed film.