Deformation behavior of a twin-roll-cast Mg-6Zn-0.5Mn-0.3Cu-0.02Zr alloy at intermediate temperatures
SCIE
SCOPUS
- Title
- Deformation behavior of a twin-roll-cast Mg-6Zn-0.5Mn-0.3Cu-0.02Zr alloy at intermediate temperatures
- Authors
- Song, SX; Horton, JA; Kim, NJ; Nieh, TG
- Date Issued
- 2007-03
- Publisher
- PERGAMON-ELSEVIER SCIENCE LTD
- Abstract
- The mechanical properties of a twin-roll-cast Mg-6Zn-0.5Mn-0.3Cu-0.02Zr were measured at temperatures from 423 to 523 K. Constant strain rate, strain-rate-change and temperature change tests were employed to characterize the plastic flow behavior of the alloy. It was observed that a in low-strain-rate and high-temperature regime the alloy follows a power-law behavior; however, the power law breaks down at high strain rates and low temperatures. Transient experiments were also conducted to identify the deformation mechanism. Published by Elsevier Ltd. on behalf of Acta Materialia Inc.
- Keywords
- magnesium alloys; twin roll cast; high temperature deformation; dislocation glide; MAGNESIUM SINGLE CRYSTALS; ELEVATED-TEMPERATURES; NONBASAL SLIP
- URI
- https://oasis.postech.ac.kr/handle/2014.oak/29458
- DOI
- 10.1016/j.scriptamat.2006.10.040
- ISSN
- 1359-6462
- Article Type
- Article
- Citation
- SCRIPTA MATERIALIA, vol. 56, no. 5, page. 393 - 395, 2007-03
- Files in This Item:
- There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.