Chemical ordering in PtNi nanocrystals

Abstract

We investigated the chemical ordering in PtNi nanocrystals fabricated on sapphire substrate using in-situ synchrotron X-ray scattering. Nanocrystals with composition close to 1:1 were ordered in the tetragonal L1(0) structure at low temperatures. The transition to disordered FCC structure occurred at around 640 degrees C and substantial hysteresis of about 50 K was observed. Nanocrystals of smaller sizes fabricated under the same conditions were Ni rich and ordered into Cu3Au type L1(2) structure. Significantly higher degree of chemical ordering was observed in L1(2) structure than in L1(0) structure. (C) 2016 Elsevier B.V. All rights reserved.