Tribological properties of HVOF-sprayed WC-Co coatings deposited from Ni-plated powders at elevated temperature

Abstract

WC-Co coatings with low degree of WC decomposition were deposited from electroless Ni-plated micro- and nano-structured feedstock powders using high velocity oxygen fuel (HVOF) spraying. Dry sliding friction and wear behavior of the resultant coatings, referred to as Ni/mc-WC and Ni/nc-WC, were investigated by using sintered alumina (Al(2)o(3)) as the mating material at 700 degrees C For the purpose of comparison, similar experiments were carried out on conventional micro- and nano-structured coatings, denoted as me-WC and nc-WC. The worn scars were examined by field emission scanning electron microscopy (FESEM) equipped with energy dispersive spectroscopy (EDS). The wear resistance of Ni/mc-WC and Ni/nc-WC coatings at 700 degrees C was found to be 45% and 72% greater than that of me-WC and nc-WC coatings, respectively. Moreover, Ni/mc-WC and Ni/nc-WC coatings exhibited a significantly lower friction coefficient with negligible fluctuations as compared to me-WC and nc-WC. The microscopic analyses of me-WC and nc-WC worn surface revealed the presence of plastically deformed and discontinuous tribofilms, made up of a mixture of MWO4/WO3 (M = Co) and Al2O3, severe cracking and delamination especially at the interface of tribofilm and the underlying surface. In contrast, examination of Ni/mc-WC and Ni/nc-WC substantiated that a large area of the coatings surface is covered by a dense and adhered MWO4-type oxide layer (M = Co, Ni), which provides a more protection against wear at elevated temperature. (C) 2017 Elsevier B.V. All rights reserved.